Parametry techniczne
| Model | Zinc oxide desulfurization adsorbent T306 |
| Color | White or light yellow |
| Shape | extrude |
| Normal size(mm) | Φ4×4-15 |
| Bulk Density(kg/L) | 1.0-1.3 |
| Crushing strength(N/cm) | ≥50 |
| Loss on Attrition(%) | ≤6 |
| Breakthrough sulfur capacity, wt％ | ≥28(350℃) ≥15(220℃) ≥10(200℃) |
| Pressure, MPa | ambient to 4.0 |
| Temperature ℃ | 180-400 |
| Space velocity, h－1 | 1000-2000（gas） |
| Sulfur in feed gas, mg/m3 | 1-20 (≤200℃) 20-100 (≤250℃) |
| Sulfur in treated stream, ppm | max0.1 |
| Saturation sulfur capacity, wt% | min30(400℃) |
| Feature and Typical Application | T306 Zinc Oxide Desulfurization Adsorbent, developed by the Northwest Research Institute of Chemical Industry, is applicable to desulfurization of residue cracking gases or syngas and purification of feed gases for organic synthesis processes. It is suitable for both higher (350-408℃) and lower(150-210℃) temperature use. It can convert some simpler organic sulfur while absorbing inorganic sulfur in gas stream. Main reaction of the desulfurization process is as follows: (1) Reaction of zinc oxide with hydrogen sulfide H2S+ZnO=ZnS+H2O (2) Reaction of zinc oxide with some simpler sulfur compounds in two possible ways: a. Organic sulfur compounds, catalyzed by zinc oxide, react with hydrogen to form hydrogen sulfide: CS2 + 4H2 = CH4 + 2H2S C2H5SH + H2 = C2H6 + H2S Then hydrogen sulfide is absorbed by zinc oxide H2S+ZnO=ZnS+H2O b. Zinc oxide reacts directly with organic sulfur compounds COS + ZnO = ZnS + CO2 T306 is an ideal desulfurization adsorbent for deep purification cases, especially those at higher temperature (350-400℃). |
| Loading | Loading depth: Higher L/D (min3) is recommended. Configuration of two reactors in series can improve utilization efficiency of the adsorbent. Loading procedure: (1)Clean the reactor before loading; (2)Put two stainless grids with smaller mesh size than the adsorbent; (3)Load a 100mm layer of Φ10—20mm refractory spheres upon the stainless grids; (4)Screen the adsorbent to remove dust; (5)Use special tool to ensure evenly distribution of the adsorbent in the bed; (6)Inspect uniformity of the bed during loading. When inside-reactor operation is needed, A wood plate should be put on the adsorbent for the operator to stand upon. (7)Install A stainless grid with small mesh size than the adsorbent and a 100mm layer of Φ20—30mm refractory spheres at the top of the adsorbent bed so as to prevent entrainment of the adsorbent and ensure even distribution of the gas stream. Note: Evenly distribution of the adsorbent is essential to its efficient operation, which should be paid close attention to. |
| Start-up | (1)Replace the system by nitrogen or other inert gases until oxygen concentration in the gas is less than 0.5%; (2)Preheat the feed stream with nitrogen or feed gas under ambient or elevated pressure; (3)Heating speed: 50℃/h from room temperature to 150℃ (with nitrogen) ; 150℃ for 2h (when heating medium is shifted to feed gas ), 30℃/h over 150℃ until required temperature is attained. (4)Adjust the pressure steadily until the operation pressure is attained. (5)After pre-heating and pressure elevation, the system should first be operated at half load for 8h. Then raise the load steadily when operation becomes stable till full-scale operation. |
| Shut-down | (1)Emergent shut-down Cut feed gas (oil) supply. Close inlet and outlet valves. Keep the temperature and pressure. If necessary ,use nitrogen or hydrogen-nitrogen gas to maintain the pressure to prevent negative pressure. (2 ) Change-over of desulfurization adsorbent Close inlet and outlet valves. Steadily lower the temperature and pressure to ambient condition. Then isolate the desulfurization reactor from the production system. Replace the reactor with air until oxygen concentration of ＞20％ is attained. Open the reactor and unload the adsorbent. (3) Equipment maintenance (overhaul) Observe the same procedure as shown above except that pressure should be lowered at 0.5MPa/10min and temperature lowered naturally. The unloaded adsorbent shall be stored in separate layers. Analyze the samples taken from each layer to determine status and service life of the adsorbent. |
| Transportation and storage | (1)The adsorbent product is packed in plastic or iron barrels with plastic lining to prevent moisture and chemical contamination. (2)Tumbling, collision and violent vibration should be avoided during transportation to prevent pulverization of the adsorbent. (3)The adsorbent product should be prevented from contact with chemicals during transportation and storage. (4)The product can be stored for 3-5 years without deterioration of its properties if appropriately sealed. |
Produkty
Sita Molekularne
- Sita molekularne 4A
- Sita molekularne 5A
- Sita molekularne 13X
- Sita molekularne 13X APG
- Sita molekularne XH-7
- Sita molekularne XH-9
- Sita molekularne do ram okiennych
- Aktywne Sproszkowane Sita Molekularne
- Węglowe Sita Molekularne
- ZSM-5 Zeolity Selektywnych Kryształów
- Sita Molekularne NaY
Aktywowany Tlenek Glinu
Katalizatory
Żel Krzemionkowy
Węgiel Aktywowany
Kulki Ceramiczne
Wypełnienia Kolumnowe
- Ceramiczne siodło Berla
- Ceramiczny pierścień z krzyżem
- Ceramiczny mini pierścień z kaskadą
- Ceramiczne Super Siodła
- Ceramiczny pierścień Palla
- Ceramiczny pierścień Raschiga
- Ceramiczny pierścień odgradzający
- Ceramiczny pierścień 3Y
- Ceramiczny pierścień kołowy
- Ceramiczne siodło Intalox
- Metalowy mini pierścień z kaskadą
- Metalowy pierścień Raschiga
- Metalowy super pierścień Raschiga
- Metalowy pierścień łuku wewnętrznego
- Metalowy pierścień sprzężony
- Metalowy Super Mini Pierścień
- Metalowy pierścień Palla
- Metalowe Super Siodła
- Metalowe siodełka Intaloxa
- Plastikowa pusta kula chroniąca przed słońcem do zbiorników
- Plastikowy płatek śniegu
- Plastikowa kulka pokrywająca powierzchnię w płynie
- Q-Pack
- Plastikowy pierścień sprężony
- Plastikowe potrójne opakowanie
- Plastikowy pierścień spiralny
- Plastikowy pierścień rozety
- Plastikowa pusta kulka pływająca
- Plastikowa wielościenna pusta kula
- Plastikowy kaskadowy mini pierścień
- Plastikowe super siodła
- Plastikowe siodła Intaloxa
- Plastikowy pierścień Pall
- Plastikowy pierścień Raschiga
- Pierścień pięciokątny
- Plastikowe VSP
- Plastikowy pierścień Hiflowa
- Plastikowy pierścień kątowy
Wypełnienia Strukturalne
- Plastikowe opakowanie strukturalne - plaster miodu
- Opakowanie z tektury falistej z blachy perforowanej
- Opakowanie strukturalne z gazy drucianej
- Ceramiczne opakowanie strukturalne
- Porcelanowy monolit o strukturze plastra miodu
- Kompaktowy kordierytowy monolit o strukturze plastra miodu
- Porowaty kordierytowy monolit o strukturze plastra miodu
Sita Molekularne do oxygeneratorów medycznych
Środek zapobiegający infekcji
Kratka ceramiczna
Karbowane Pierścienie Rashiga
Sprężynki pryzmatyczne
Kaldens
Produkty
Jesteśmy na bieżąco z nowinkami technicznymi i wdrażamy je w ramach naszej oferty.
%
Satysfakcji
Nasze produkty, są najwyższej możliwej jakości. Kupując u nas, kupujesz bezpiecznie.
Lat doświadczenia
O naszych produktach wiemy wszystko. Praktyczna wiedza nabywana przez lata obecności w branży.
Państwa
Nasza Marka gościła w krajach na całym świecie. Produkty dostarczamy m.in. do Niemiec, Szwecji i Stanów Zjednoczonych.
HurtGral - Twój dostawca sit molekularnych.
Kontakt
Jeżeli chcą Państwo omówić swoje zamówienie, zapytać o produkty lub omówić specyfikację produktów zapraszamy do kontaktu.
Zadzwoń pod numer +48 792 020 580 lub skorzystaj z formularza kontaktowego.
HurtGral - Twój dostawca sit molekularnych.
Wypełnienia ceramiczne, drożdże, enzymy, dodatki dla przemysłu spożywczego.